Abstract: In the present study, an ecofriendly biocomposite namely calcium alginate immobilized Ammi Visnaga (Khella) extraction waste (SWAV/CA) was prepared by electrostatic extrusion method and used on the cadmium biosorption from aqueous phase with and without the assistance of ultrasound in batch conditions. The influence of low frequency ultrasound (37 and 80 KHz) on the cadmium biosorption kinetics was studied. The obtained results show that the ultrasonic irradiation significantly enhances and improves the efficiency of the cadmium removal. The Pseudo first order, Pseudo-second-order, Intraparticle diffusion, and Elovich models were evaluated using the non-linear curve fitting analysis method. Modeling of kinetic results shows that biosorption process is best described by the pseudo-second order and Elovich, in both the absence and presence of ultrasound.
Abstract: A biocompatible ferrofluid have been prepared by coprecipitation
of FeCl2.4H2O and FeCl3.6H2O under ultrasonic
irradiation and with NaOH as alkaline agent. Cystein was also used
as capping agent in the solution. Magnetic properties of the produced
ferrofluid were then determined by VSM test and magnetite
nanoparticles were characterized by XRD and TEM techniques. The
effect of surfactant to Fe ion weight ratio was also studied during this
project by using two different amount of Dextran. Results showed the
presence of a biocompatible superparamagnetic ferrofluid including
magnetite nanoparticles with particle size ranging under 20 nm. The
increase in the surfactant content results in the narrowing of the size
distribution and reduction of the particle size and more solution
stability.