Abstract: Concrete is found to undergo degradation when
subjected to elevated temperatures and loose substantial amount of its
strength. The loss of strength in concrete is mainly attributed to
decomposition of C-S-H and release of physically and chemically
bound water, which begins when the exposure temperature exceeds
100°C. When such a concrete comes in contact with moisture, the
cement paste is found rehydrate and considerable amount of strength
lost is found to recover. This paper presents results of an
experimental program carried out to investigate the effect of recuring
on strength gain of OPC concrete specimens subjected to elevated
temperatures from 200°C to 800°C, which were subjected to
retention time of two hours and four hours at the designated
temperature. Strength recoveries for concrete subjected to 7
designated elevated temperatures are compared. It is found that the
efficacy of recuring as a measure of strength recovery reduces with
increase in exposure temperature.
Abstract: Strength recovery effect from the residual-state of shear is not well address in scientific literature. Torsional ring shear strength recovery tests on kaolin clay using rest periods up to 30 days are performed at the effective normal stress 100kN/m2. Test results shows that recovered strength measured in the laboratory is slightly noticeable after rest period of 3 days, but recovered strength lost after very small shear displacement. This paper mainly focused on the strength recovery phenomenon from the residual strength of kaolin clay based on torsional ring shear test results. Mechanisms of recovered strength are also discussed.