Abstract: In the present study, the reactions involving 4-bromo-2,6-bis-hydroxymethyl-phenol (BBHMP) and nicotinamide (NA) in the presence of Pd(II) ions were investigated. Optimum conditions for the reactions were established as pH = 7 and λ = 450 nm. According to absorbance measurements, the molar ratio of BBHMP: NA: Pd2+ was found to be 1: 2: 2. As a result of physicochemical, spectrophotometric and thermal analyses, the reactions of BBHMP and NA with Pd(II) are complexation reactions and one molecule of BBHMP and two molecules of NA react with two molecules of the Pd(II) ion.
Abstract: Synthesizing supercritical carbon dioxide (scCO2) soluble precursors would be helpful for many processes of material syntheses based on scCO2. Ligand (amphi-(1Z, 2Z)-N-(2-fluoro-3-(trifluoromethyl) phenyl)-N'-hydroxy-2-(hydroxyimino) were synthesized from chloro glyoxime and flourus aniline and Pd(II) complex (precursor) prepared. For scCO2 deposition method, organometallic precursor was dissolved in scCO2 and impregnated onto the SBA-15 at 90 °C and 3000 psi. Then the organometallic precursor was reduced with H2 in the CO2 mixture (150 psi H2 + 2850 psi CO2). Pd deposited support material was characterized by ICP-OES, XRD, FE-SEM, TEM and EDX analyses. The Pd loading of the prepared catalyst, measured by ICP-OES showed a value of about 1.64% mol/g Pd of catalyst. Average particle size was found 5.3 nm. The catalytic activity of prepared catalyst was investigated over Suzuki-Miyaura C-C coupling reaction in different solvent with K2CO3 at 50 oC. The conversion ratio was determined by gas chromatography.
Abstract: The polyfunctional and highly reactive bio-polymer,
the chitosan was first regioselectively converted into dialkylated
chitosan using dimsyl anionic solution(NaH in DMSO) and
bromodecane after protecting amino groups by phthalic anhydride.
The dibenzo-18-crown-6-ether, on the other hand, was converted into
its carbonyl derivatives via Duff reaction prior to incorporate into
chitosan by Schiff base formation. Thus formed diformylated
dibenzo-18-crown-6-ether was condensed with lipophilic chitosan to
prepare the novel solvent extraction reagent. The products were
characterized mainly by IR and 1H-NMR. Hence, the multidentate
crown ether-embedded polyfunctional bio-material was tested for
extraction of Pd(II) and Pt(IV) in aqueous solution.