Abstract: Automotive light weighting is of major prominence in the current times due to its contribution in improved fuel economy and reduced environmental pollution. Various arc welding technologies are being employed in the production of automobile components with reduced weight. The present study is of practical importance since it involves preferential substitution of Zinc coated mild steel with a light weight alloy such as 6061 Aluminium by means of Gas Metal Arc Welding (GMAW) – Brazing technique at different processing parameters. However, the fabricated joints have shown the generation of Al – Fe layer at the interfacial regions which was confirmed by the Scanning Electron Microscope and Energy Dispersion Spectroscopy. These Al-Fe compounds not only affect the mechanical strength, but also predominantly deteriorate the corrosion resistance of the joints. Hence, it is essential to understand the phases formed in this layer and their crystal structure. Micro area X - ray diffraction technique has been exclusively used for this study. Moreover, the crevice corrosion analysis at the joint interfaces was done by exposing the joints to 5 wt.% FeCl3 solution at regular time intervals as per ASTM G 48-03. The joints have shown a decreased crevice corrosion resistance with increased heat intensity. Inner surfaces of welds have shown severe oxide cracking and a remarkable weight loss when exposed to concentrated FeCl3. The weight loss was enhanced with decreased filler wire feed rate and increased heat intensity.
Abstract: Shaped Metal Deposition (SMD) in additive layered manufacturing technique is a promising alternative to traditional manufacturing used for manufacturing large, expensive metal components with complex geometry in addition to producing free structures by building materials in a layer by layer technique. The present paper is a comprehensive review of the literature and the latest rapid manufacturing technologies of the SMD technique. The aim of this paper is to comprehensively review the most prominent facts that researchers have dealt with in the SMD techniques especially those associated with the cold wire feed. The intent of this study is to review the literature presented on metal deposition processes and their classifications, including SMD process using Wire + Arc Additive Manufacturing (WAAM) which divides into wire + tungsten inert gas (TIG), metal inert gas (MIG), or plasma. This literary research presented covers extensive details on bead geometry, process parameters and heat input or arc energy resulting from the deposition process in both cases MIG and Tandem-MIG in SMD process. Furthermore, SMD may be done using Single Wire-MIG (SW-MIG) welding and SMD using Double Wire-MIG (DW-MIG) welding. The present review shows that the method of deposition of metals when using the DW-MIG process can be considered a distinctive and low-cost method to produce large metal components due to high deposition rates as well as reduce the input of high temperature generated during deposition and reduce the distortions. However, the accuracy and surface finish of the MIG-SMD are less as compared to electron and laser beam.
Abstract: Friction Stir Welding (FSW) is a solid-state welding technique that can join material without melting the plates to be welded. In this work, we are interested to demonstrate the potentiality of FSW for joining the heat-treatable aluminum alloy 2024-T3 which is reputed as difficult to be welded by fusion techniques. Thereafter, the FSW joint is compared with another one obtained from a conventional fusion process Tungsten Inert Gas (TIG). FSW welds are made up using an FSW tool mounted on a milling machine. Single pass welding was applied to fabricated TIG joint. The comparison between the two processes has been made on the temperature evolution, mechanical and microstructure behavior. The microstructural examination revealed that FSW weld is composed of four zones: Base metal (BM), Heat affected zone (HAZ), Thermo-mechanical affected zone (THAZ) and the nugget zone (NZ). The NZ exhibits a recrystallized equiaxed refined grains that induce better mechanical properties and good ductility compared to TIG joint where the grains have a larger size in the welded region compared with the BM due to the elevated heat input. The microhardness results show that, in FSW weld, the THAZ contains the lowest microhardness values and increase in the NZ; however, in TIG process, the lowest values are localized on the NZ.
Abstract: In this study, the butt welding of the commercial AZ31 magnesium alloy sheets have been carried out by using Tungsten Inert Gas (TIG) welding process with alternative and pulsed current. Welded samples were examined with regards to hardness and microstructure. Despite some recent developments in welding of magnesium alloys, they have some problems such as porosity, hot cracking, oxide formation and so on. Samples of the welded parts have undergone metallographic and mechanical examination. Porosities and homogeneous micron grain oxides were rarely observed. Orientations of the weld microstructure in terms of heat transfer also were rarely observed and equiaxed grain morphology was dominant grain structure as in the base metal. As results, fusion zone and few locations of the HAZ of the welded samples have shown twin’s grains. Hot cracking was not observed for any samples. Weld bead geometry of the welded samples were evaluated as normal according to welding parameters. In the results, conditions of alternative and pulsed current and the samples were compared to each other with regards to microstructure and hardness.
Abstract: Friction stir welding and tungsten inert gas welding
techniques were employed to weld armor grade aluminum alloy to
investigate the effect of welding processes on tensile behavior of
weld joints. Tensile tests, Vicker microhardness tests and optical
microscopy were performed on developed weld joints and base metal.
Welding process influenced tensile behavior and microstructure of
weld joints. Friction stir welded joints showed tensile behavior better
than tungsten inert gas weld joints.
Abstract: Tungsten Inert Gas (TIG) welding is a high quality welding process used to weld the thin metals and their alloy. 5083 Aluminium alloys play an important role in engineering and metallurgy field because of excellent corrosion properties, ease of fabrication and high specific strength coupled with best combination of toughness and formability.
TIG welding technique is one of the precise and fastest processes used in aerospace, ship and marine industries. TIG welding process is used to analyze the data and evaluate the influence of input parameters on tensile strength of 5083 Al-alloy specimens with dimensions of 100mm long x 15mm wide x 5mm thick. Welding current (I), gas flow rate (G) and welding speed (S) are the input parameters which effect tensile strength of 5083 Al-alloy welded joints. As welding speed increased, tensile strength increases first till optimum value and after that both decreases by increasing welding speed further. Results of the study show that maximum tensile strength of 129 MPa of weld joint are obtained at welding current of 240 Amps, gas flow rate of 7 Lt/min and welding speed of 98 mm/min. These values are the optimum values of input parameters which help to produce efficient weld joint that have good mechanical properties as a tensile strength.
Abstract: This article deals with the carbon nanotubes (CNT) synthesized from a novel precursor, sugar cane and Anodic Aluminum Oxide (AAO). The objective was to produce CNTs to be used as catalyst supports for Proton Exchange Membranes. The influence of temperature, inert gas flow rate and concentration of the precursor is presented. The CNTs prepared were characterized using TEM, XRD, Raman Spectroscopy, and the surface area determined by BET. The results show that it is possible to form CNT from sugar cane by pyrolysis and the CNTs are the type multi-walled carbon nanotubes. The MWCNTs are short and closed at the two ends with very small surface area of SBET= 3.691m,/g.
Abstract: Experimental study was conducted to assess personal welding fumes exposure toward welders during an aluminum metal inert gas (MIG) process. The welding process was carried out by a welding machine attached to a Computer Numerical Control (CNC) workbench. A dummy welder was used to replicate welder during welding works and was attached with sampling pumps and filter cassettes for welding fumes sampling. Direct reading instruments to measure air velocity, humidity, temperature and particulate matter with diameter size 10µm or less (PM10) were located behind the dummy welder and parallel to the neck collar level to make sure the measured welding fumes exposure were not being influenced by other factors. Welding fumes exposure during standing and sitting position with and without the usage of local exhaust ventilation (LEV) was investigated. Welding fume samples were then digested and analyzed by using inductively coupled plasma mass spectroscopy (ICP-MS) according to ASTM D7439-08 method. The results of the study showed the welding fume exposure during sitting was lower compared to standing position. LEV helped reduce aluminum and lead exposure to acceptable levels during standing position. However during sitting position reduction of exposure was smaller. It can be concluded that welder position and the correct positioning of LEV should be implemented for effective exposure reduction.
Abstract: Understanding of how and where NOx formation
occurs in industrial burner is very important for efficient and clean
operation of utility burners. Also the importance of this problem is
mainly due to its relation to the pollutants produced by more burners
used widely of gas turbine in thermal power plants and glass and steel
industry.
In this article, a numerical model of an industrial burner operating
in MILD combustion is validated with experimental data.. Then
influence of air flow rate and air temperature on combustor
temperature profiles and NOX product are investigated. In order to
modification this study reports on the effects of fuel and air dilution
(with inert gases H2O, CO2, N2), and also influence of lean-premixed
of fuel, on the temperature profiles and NOX emission.
Conservation equations of mass, momentum and energy, and
transport equations of species concentrations, turbulence, combustion
and radiation modeling in addition to NO modeling equations were
solved together to present temperature and NO distribution inside the
burner.
The results shows that dilution, cause to a reduction in value of
temperature and NOX emission, and suppresses any flame
propagation inside the furnace and made the flame inside the furnace
invisible. Dilution with H2O rather than N2 and CO2 decreases further
the value of the NOX. Also with raise of lean-premix level, local
temperature of burner and the value of NOX product are decreases
because of premixing prevents local “hot spots" within the combustor
volume that can lead to significant NOx formation. Also leanpremixing
of fuel with air cause to amount of air in reaction zone is
reach more than amount that supplied as is actually needed to burn
the fuel and this act lead to limiting NOx formation
Abstract: Synthesis gas manufacturing by steam reforming of hydrocarbons is an important industrial process. High endothermic nature of the process makes it one of the most cost and heat intensive processes. In the present work, composite effect of different inert gases on synthesis gas yield, feed gas conversion and temperature distribution along the reactor length has been studied using a heterogeneous model. Mathematical model was developed as a first stage and validated against the existing process models. With the addition of inert gases, a higher yield of synthesis gas is observed. Simultaneously the rector outlet temperature drops to as low as 810 K. It was found that Xenon gives the highest yield and conversion while Helium gives the lowest temperature. Using Xenon inert gas 20 percent reduction in outlet temperature was observed compared to traditional case.