Abstract: The removal of lead ion (Pb2+) from aqueous solution by activated carbon with phosphoric acid activation employing mangrove propagule as precursor was investigated in a batch adsorption system. Batch studies were carried out to address various experimental parameters including pH and contact time. The Langmuir and Freundlich models were able to describe the adsorption equilibrium, while the pseudo first order and pseudo second order models were used to describe kinetic process of Pb2+ adsorption. The results show that the adsorption data are seen in accordance with Langmuir isotherm model and pseudo-second order kinetic model.
Abstract: The Iranian bentonite was first characterized by
Scanning Electron Microscopy (SEM), Inductively Coupled Plasma
mass spectrometry (ICP-MS), X-ray fluorescence (XRF), X-ray
Diffraction (XRD) and BET. The bentonite was then treated
thermally between 150°C-250°C at 15min, 45min and 90min and
also was activated chemically with different concentration of
sulphuric acid (3N, 5N and 10N). Although the results of thermal
activated-bentonite didn-t show any considerable changes in specific
surface area and Cation Exchange Capacity (CEC), but the results of
chemical treated bentonite demonstrated that such properties have
been improved by acid activation process.
Abstract: Bentonitic material from South Aswan, Egypt was evaluated in terms of mineral-ogy and chemical composition as bleaching clay in refining of transformer oil before and after acid activation and thermal treatment followed by acid leaching using HCl and H2SO4 for different contact times. Structural modification and refining power of bento-nite were investigated during modification by means of X-ray diffraction and infrared spectroscopy. The results revealed that the activated bentonite could be used for refining of transformer oil. The oil parameters such as; dielectric strength, viscosity and flash point had been improved. The dielectric breakdown strength of used oil increased from 29 kV for used oil treated with unactivated bentonite to 74 kV after treatment with activated bentonite. Kinematic Viscosity changed from 19 to 11 mm2 /s after treatment with activated bentonite. However, flash point achieved 149 ºC.