Single-Walled Carbon Nanotube Synthesis by Chemical Vapor Deposition Using Platinum-Group Metal Catalysts

Single-walled carbon nanotubes (SWCNTs) are generally synthesized by chemical vapor deposition (CVD) using Fe, Co, and Ni as catalysts. However, due to the Ostwald ripening of metal catalysts, the diameter distribution of the grown SWCNTs is considerably wide (>2 nm), which is not suitable for electronics applications. In addition, reduction in the growth temperature is desirable for fabricating SWCNT devices compatible with the LSI process. Herein, we performed SWCNT growth by alcohol catalytic CVD using platinum-group metal catalysts (Pt, Rh, and Pd) because these metals have high melting points, and the reduction in the Ostwald ripening of catalyst particles is expected. Our results revealed that web-like SWCNTs were obtained from Pt and Rh catalysts at growth temperature between 500 °C and 600 °C by optimizing the ethanol pressure. The SWCNT yield from Pd catalysts was considerably low. By decreasing the growth temperature, the diameter and chirality distribution of SWCNTs from Pt and Rh catalysts became small and narrow. In particular, the diameters of most SWCNTs grown using Pt catalysts were below 1 nm and their diameter distribution was considerably narrow. On the contrary, SWCNTs can grow from Rh catalysts even at 300 °C by optimizing the growth condition, which is the lowest temperature recorded for SWCNT growth. Our results demonstrated that platinum-group metals are useful for the growth of small-diameter SWCNTs and facilitate low-temperature growth.





References:
[1] S. Iijima, and T. Ichihashi, “Single-shell carbon nanotubes of 1-nm diameter,” Nature, vol. 363, pp. 603-605, 1993.
[2] R. Saito, G. Dresslehaus, and M. S. Dresselhaus, “Physical Properties of Carbon Nanotubes,” Imperial College Press, London, 1998.
[3] M. Meyyappan, “Carbon Nanotubes: Science and Applications,” CRC Press, FL; Boca Raton, 2005.
[4] S. J. Trans, M. H. Devoret, H. J. Dai, A. Thess, R. E. Smalley, L. J. Geerligs, and C. Deller, “Individual single-wall carbon nanotubes as quantum wires,” Nature, vol. 386, pp.474-477, 1997.
[5] J. Robertson, G. Zhong, S. Hofmann, B. C. Bayer, C. S. Esconjauregui, H. Telg, and C. Thomsen, “Use of carbon nanotubes for VLSI interconnects,” Diam. Relat. Mater., vol. 18, pp. 957-962, 2009
[6] J. Chen, V. Perebeinos, M. Freitag, J. Tsang, Q. Fu, J. Liu, and P. Avouris, “Bright infrared emission from electrically induced excitons in carbon nanotubes,” Science, vol. 310, pp. 1171-1174, 2005.
[7] A. Javey, J. Guo, Q. Wang, M. Lundstrom, and H. Dai, “Ballistic carbon nanotube field-effect transistors,” Nature, vol. 424, pp. 654-657, 2003.
[8] T. Dürkop, S. A. Getty, E. Cobas, and M. S. Fuhrer, “Extraordinary mobility in semiconducting carbon nanotubes,” Nano Lett., vol. 4, pp. 35-39, 2004.
[9] S. Hong, and S. Myung, “Nanotube electronics: a flexible approach to mobility,” Nat. Nanotech., vol. 2, pp. 207-208, 2007.
[10] S. J. Tans, A. R. M. Vershueren, and C. Dekker, “Room-temperature transistor based on a single carbon nanotube,” Nature, vol. 393, pp. 49-52, 1998.
[11] S. J. Wind, J. Appenzeller, R. Martel, V. Derycke, and P. Avouris, “Vertical scaling of carbon nanotube field-effect transistors using top gate electronics,” Appl. Phys. Lett., vol. 80, pp. 3817-3819, 2002.
[12] D. Kondo, S. Sato, A. Kawarada, and Y. Awano, “Selective growth of vertically aligned double- and single-walled carbon nanotubes on a substrate at 590°C,” Nanotechnol., vol. 19, pp. 435601, 2008.
[13] T. Iwasaki, J. Robertson, and H. Kawarada, “Mechanism analysis of interrupted growth of single-walled carbon nanotube arrays,” Nano Lett., vol. 8, pp. 886-890, 2008.
[14] G. Girishkumar, K. Vinodgopal, and P. V. Kamat, “Carbon nanostructure in portable fuel cells: single-walled carbon nanotube electrodes for methanol oxidation and oxygen reduction,” J. Phys. Chem. B, vol. 108, pp. 19960-19966, 2004.
[15] M. W. Rowell, M. A. Topinka, M. D. McGehee, H.-J. Prall, G. Dennler, N. S. Sariciftci, L. Hu, and G. Gruner, “Organic solar cells with carbon nanotube network electrodes,” Appl. Phys. Lett., vol. 88, pp. 233506, 2006.
[16] K. Hata, D. N. Futaba, K. Mizuno, T. Namai, M. Yumura, and S. Iijima, “Water-assisted highly efficient synthesis of impurity-free single-walled carbon nanotube,” Science, vol. 306, pp. 1362-1364, 2004.
[17] G. Zhong, T. Iwasaki, J. Robertson, and H. Kawarada, “Growth kinetics of 0.5 cm vertically aligned single-walled carbon nanotubes,” J. Phys. Chem. B, vol. 111, pp. 1907-1910, 2007.
[18] S. Maruyama, R. Kojima, Y. Miyauchi, S. Chiashi, and M. Kouhno, “Low-temperature synthesis of high-purity single-walled carbon nanotubes from alcohol,” Chem. Phys. Lett., vol. 360, pp. 229-234, 2002.
[19] M. Fouquet, B. C. Bayer, S. Esconjauregui, R. Blume, J. H. Warner, S. Hofmann, R. Schlögl, C. Thomsen, and J. Robertson, “Highly chiral-selective growth of single-walled carbon nanotubes with a simple monometallic Co catalysts,” Phys. Rev. B, vol. 85, pp. 235411, 2002.
[20] M. Paillet, V. Jourdain, P. Poncharal, J.-L. Sauvajol, and A. Zahab, “Versatile synthesis of individual single-walled carbon nanotubes from nickel nanoparticles for the study of their physical properties,” J. Phys. Chem. B, vol. 108, pp. 17112-17118, 2004.
[21] E. Mora, J. M. Pigos, F. Ding, B. I. Yakobson, and A. R. Harutyunyan, “Low-temperature single-wall carbon nanotubes synthesis: Feedstock decomposition limited growth,” J. Am. Chem. Soc., vol. 130, pp. 11840-11841, 2008.
[22] B. Wang, C. H. Patrick Poa, L. Wei, L.-J. Li, Y. Yang, and Y. Chen, “(n, m) selectivity of single-walled carbon nanotubes by different carbon precursors on Co-Mo catalysts,” J. Am. Chem. Soc., vol. 129, pp. 9014-9019, 2007.
[23] Z. Ghorannevis, T. Kato, Y. Kaneko, and R. Hatakeyama, “Narrow-chirality distributed single-walled carbon nanotube growth from nonmagnetic catalyst,” J. Am. Chem. Soc., vol. 132, pp. 9570-9572, 2010.
[24] B. Lie, W. Ren, S. Li, C. Liu, and H.-M. Cheng, “High temperature selective growth of single-walled carbon nanotubes with a narrow chirality distribution from a CoPt bimetallic catalyst,” Chem. Commun., vol. 48, pp. 2409-2411, 2012.
[25] T. Maruyama, “Current status of single-walled carbon nanotube synthesis from metal catalysts by chemical vapor deposition,” Mater. Express, vol. 8, pp. 1-20, 2018.
[26] T. Maruyama, H. Kondo, R. Ghosh, A. Kozawa, S. Naritsuka, Y. Iizumi, T. Okazaki, and S. Iijima, “Single-walled carbon nanotube synthesis using Pt catalysts under low ethanol pressure via cold-wall chemical vapor deposition in high vacuum,” Carbon, vol. 96, pp. 6-13, 2016.
[27] T. Maruyama, A. Kozawa, T. Saida, S. Naritsuka, and S. Iijima, “Low temperature growth of single-walled carbon nanotubes from Rh catalysts,” Carbon, vol. 116, pp. 128-132, 2017.
[28] A. Jorio, R. Saito, J. H. Hafner, C. M. Liever, M. Hunter, T. McClure, G. Dresselhaus, and M. S. Dresselhaus, “Structural (n, m) determination of isolated single-wall carbon nanotubes by resonant Raman scattering,” Phys. Rev. B, vol. 86, pp. 1118-1121, 2001.
[29] E. Vesselli, A. Baraldi, G. Comelli, S. Lizzit, and R. Rosei, “Ethanol decomposition: C-C cleavage selectivity on Rh(111),” ChemPhysChem, vol. 5, pp. 1133-1140, 2004.
[30] J. H. Wang, C. S. Lee, M. C. Lin, “Mechanism of ethanol reforming: theoretical foundations,” J. Phys. Chem. C, vol. 113, pp. 6681-6688, 2009.
[31] C. L. Cheung, A. Kurtz, H. Park, and C. M. Liever, “Diameter-controlled synthesis of carbon nanotubes,” J. Phys. Chem. B, vol. 106, pp. 2429-2433, 2002.
[32] M. Paillet, V. Joudain, P. Poncharal, J.-L. Sauvajol, and A. Zahab, “Versatile synthesis of individual single-walled carbon nanotubes from nickel nanoparticles for the study of their physical properties,” J. Phys. Chem. B, vol. 108, pp. 17112-17118, 2004.