Abstract: A biocompatible ferrofluid have been prepared by coprecipitation
of FeCl2.4H2O and FeCl3.6H2O under ultrasonic
irradiation and with NaOH as alkaline agent. Cystein was also used
as capping agent in the solution. Magnetic properties of the produced
ferrofluid were then determined by VSM test and magnetite
nanoparticles were characterized by XRD and TEM techniques. The
effect of surfactant to Fe ion weight ratio was also studied during this
project by using two different amount of Dextran. Results showed the
presence of a biocompatible superparamagnetic ferrofluid including
magnetite nanoparticles with particle size ranging under 20 nm. The
increase in the surfactant content results in the narrowing of the size
distribution and reduction of the particle size and more solution
stability.