Abstract: Fatigue behaviors of Lead Zirconate Titanate (PZT)
ceramics under different amplitude of bipolar electrical loads have
been investigated. Fatigue behavior is represented by the change of
hysteresis loops and remnant polarization. Three levels of electrical
load amplitudes (1.00, 1.25 and 1.50 kV /mm) were applied in this
experimental. It was found that the remnant polarization decreased
significantly with the number of loading cycles. The degree of fatigue
degradation depends on the amplitude of electric field. The higher
amplitude exhibits the greater fatigue degradation.