Abstract: Some of the main causes for degradation of polymeric materials are thermal aging, hydrolysis, oxidation or chemical degradation by acids, alkalis or water. The first part of this paper provides a brief summary of advances in technology, methods and specification of composite materials for relining as a rehabilitation technique for sewage systems. The second part summarizes an investigation on frequently used composite materials for relining in Sweden, the rubber filled epoxy composite and reinforced polyester composite when they were immersed in deionized water or in dry conditions, and elevated temperatures up to 80°C in the laboratory. The tests were conducted by visual inspection, microscopy, Dynamic Mechanical Analysis (DMA), Differential Scanning Calorimetry (DSC) as well as mechanical testing, three point bending and tensile testing.
Abstract: Pipe failure and leakage is a problematic issue and the
traditional solution of replacing the pipes is costly and time
consuming. Rehabilitation by relining materials based on polymer
composites is an alternative solution towards the degradation problem
of the old piping. This paper provides a brief summary of advances in
technology, methods and materials for relining as well as a summary
of the degradation analyses of the two main composite materials used
for relining, rubber filled epoxy and reinforced polyester baltoflake
when they are exposed in deionized water and elevated temperature
up to 80°C for a duration of 2-14 months in the laboratory.