Wet Strength Improvement of Pineapple Leaf Paper for Evaporative Cooling Pad

This research aimed to modify pineapple leaf paper (PALP) for using as wet media in the evaporation cooling system by improving wet mechanical property (tensile strength) without compromising water absorption property. Polyamideamineepichorohydrin resin (PAE) and carboxymethylcellulose (CMC) were used to strengthen the paper, and the PAE and CMC ratio of 80:20 showed the optimum wet and dry tensile index values, which were higher than those of the commercial cooling pad (CCP). Compared with CCP, PALP itself and all the PAE/CMC modified PALP possessed better water absorption. The PAE/CMC modified PALP had potential to become a new type of wet media.

Factors Affecting Low Back Pain during Breastfeeding of Thai Women

Breastfeeding has been receiving much attention of late. Prolonged sitting for breastfeeding often results in back pain of the mothers. This paper reports the findings of a study on the effect of some factors, especially lumbar support, on back pain of breastfeeding mothers. The results showed that the use of lumbar support can reduce back pain of breastfeeding mothers significantly. Back pain was found to increase with breastfeeding time and the rate of increase was lower when lumbar supports were used. When lumbar support thickness was increased gradually from zero (no support) to 11 cm., the degree of low back pain decreased; rapidly at first, then slowly, and leveled off when the thickness reached 9 cm. Younger mothers were less prone to back pain than older mothers. The implications of the findings are discussed.

Effects of Sodium Bicarbonate Content and Vulcanization Method on Properties of NBR/PVC Thermal Insulator Foam

In this research sodium bicarbonate (NaHCO3) was introduced to generate carbon dioxide gas (CO2) to the existing nitrogen gas (N2) of elastomeric foam, to lower thermal conductivity (K). Various loadings of NaHCO3 (0 to 60 phr) were added into the azodicarbonamide (AZC)-containing compound and its properties were then determined. Two vulcanization methods, i.e., hot air and infrared (IR), were employed and compared in this study. Results revealed that compound viscosity tended to increase slightly with increasing NaHCO3 content but cure time was delayed. The effect of NaHCO3 content on thermal conductivity depended on the vulcanization method. For hot air method, the thermal conductivity was insignificantly changed with increasing NaHCO3 up to 40 phr whereas it tended to decrease gradually for IR method. At higher NaHCO3 content (60 phr), unexpected increase of thermal conductivity was observed. The water absorption was also determined and foam structures were then used to explain the results.