Abstract: Methanol-to-propylene conversion was carried out in a continuous-flow fixed-bed reactor over nano-sized HZSM-5 zeolites. The HZSM-5 catalysts were synthesized with different Si/Al ratio and silicon sources, and treated with NaOH. The structural property, morphology, and acidity of catalysts were measured by XRD, N2 adsorption, FE-SEM, TEM, and NH3-TPD. The results indicate that the increment of Si/Al ratio decreased the acidity of catalysts and then improved propylene selectivity, while silicon sources had slight impact on the acidity but affected the product distribution. The desilication after alkali treatment could increase intracrystalline mesopores and enhance propylene selectivity.
Abstract: HZSM-5 zeolites modified by iron and phosphorus
were applied in catalytic cracking of butene. N2 adsorption and
NH3-TPD were employed to measure the structure and acidity of
catalysts. The results indicate that increasing phosphorus loading
decreased surface area, pore volume and strong acidity of catalysts.
The addition of phosphorus significantly decreased butene conversion
and promoted propylene selectivity. The catalytic performance of
catalyst was strongly dependent on the reaction conditions.
Appropriate reaction conditions could suppress side reactions and
enhance propylene selectivity.
Abstract: Catalytic cracking of butene to propylene was carried out in a continuous-flow fixed-bed reactor over HZSM-5 catalysts modified by nickel and phosphorus. The structure and acidity of catalysts were measured by N2 adsorption, NH3-TPD and XPS. The results revealed that surface area and strong acid sites both decreased with increasing phosphorus loadings. The increment of phosphorus loadings reduced the butene conversion but enhanced the propylene selectivity and catalyst stability.