Abstract: The present study deals with the characterization of
CrSiN coatings obtained by PVD magnetron sputtering systems.
CrSiN films were deposited with different Si contents, in order to
check the effect of at.% variation on the different properties of the
Cr–N system. Coatings were characterized by scanning electron
microscopy (SEM) for thickness measurements, X-ray diffraction.
Surface morphology and the roughness characteristics were explored
using AFM, Mechanicals properties, elastic and plastic deformation
resistance of thin films were investigated using nanoindentation test. We observed that the Si addition improved the hardness and the
Young’s modulus of the Cr–N system. Indeed, the hardness value is
18,56 GPa for CrSiN coatings. Besides, the Young’s modulus value
is 224,22 GPa for CrSiN coatings for Si content of 1.2 at.%.
Abstract: These Monolayer and multilayer coatings of CrN and
AlCrN deposited on 100Cr6 (AISI 52100) substrate by PVD
magnetron sputtering system. The microstructures of the coatings
were characterized using atomic force microscopy (AFM). The AFM
analysis revealed the presence of domes and craters that are
uniformly distributed over all surfaces of the various layers.
Nanoindentation measurement of CrN coating showed maximum
hardness (H) and modulus (E) of 14 GPa and 190 GPa, respectively.
The measured H and E values of AlCrN coatings were found to be 30
GPa and 382 GPa, respectively. The improved hardness in both the
coatings was attributed mainly to a reduction in crystallite size and
decrease in surface roughness. The incorporation of Al into the CrN
coatings has improved both hardness and Young’s modulus.