Abstract: In recent years, the use of the aluminum based alloys
in the industry and technology are increasing. Alloying elements in
aluminum have further been improving the strength and stiffness
properties that provide superior compared to other metals. In this
study, investigation of physical properties (microstructure,
microhardness, tensile strength, electrical conductivity and thermal
properties) in the Al-12.6wt.%Si-%2wt.Ni ternary alloy were
investigated. Al-Si-Ni alloy was prepared in vacuum atmosphere. The
samples were directionally solidified upwards with different growth
rate V (8.3−165.45 μm/s) at constant temperature gradient G (7.73
K/mm). The flake spacings (λ), microhardness (HV), ultimate tensile
strength (σ), electrical resistivity (ρ) and thermal properties (H, Cp,
Tm) of the samples were measured. Influence of the growth rate and
spacings on microhardness, ultimate tensile strength and electrical
resistivity were investigated and relationships between them were
obtained. According to results, λ values decrease with increasing V,
but HV, σ and ρ values increase with increasing V. Variations of
electrical resistivity (ρ) of solidified samples were also measured.
The enthalpy of fusion (H) and specific heat (Cp) for the alloy was
also determined by differential scanning calorimeter (DSC) from
heating trace during the transformation from liquid to solid. The
results in this work were compared with the previous similar
experimental results.