Abstract: Orthodontic restorative materials are widely used for the direct restoration of teeth or for cosmetic dentistry purposes. These materials have helped to solve many dental problems, providing healthy and beautiful smiles for many patients. In this study, we aimed to investigate whether the pH value has an effect on the surface structure of a nanohybrid composite material. Five different types of highly consumed beverages were selected to examine their effect on the surface structure of the nanohybrid composite material. The beverages had different pH values in the range of 3–6, i.e., they were all acidic. The material was investigated under the hardest conditions of surface exposure to the drinks by immersing the material for a long period. The specimens were examined using scanning electron microscopy (SEM) at different magnifications to investigate the effect of these beverages on the morphology of the nanohybrid composite material discs. All specimens showed an effect including pores, cracks, protrusions, and surface roughness as a result of the beverages. The degree of effect differed from one experimental group to another, but there was no relationship between the pH (acidity) value and the degree of effect on the surface structure of the specimens.
Abstract: The recycling process of Tungsten alloy (Swarf) by
oxidation reduction technique have been investigated. The reduced
powder was pressed under a pressure 20Kg/cm2 and sintered at
1150°C in dry hydrogen atmosphere. The particle size of the recycled
alloy powder was 1-3 μm and the shape was regular at a reduction
temperature 800°C. The chemical composition of the recycled alloy
is the same as the primary Swarf.